A new method developed to produce precursors for high-strength carbon fibers processing
Carbon fiber is an important structural material of the 21st century. Due to its high strength, which is not inferior to metal alloys, in combination with low specific weight and high oxidative stability, it is an indispensable material for airspace and shipbuilding industry, construction, medicine, sports industry, and in other high-tech industry sectors.
The main method of carbon fiber production involves heat treatment of synthetic fibers obtained from polymers based on acrylonitrile. The quality of the finished carbon fiber and its strength characteristics largely depend on the composition and molecular weight characteristics of the polymer raw materials (precursors) from which the fiber is extruded. Therefore, the important tasks in the field of synthesis of precursors for carbon fibers are to search for new compositions for copolymerization, and to develop effective polymerization methods that enable the control of the molecular weight of the samples obtained.
One of the latest achievements in modern synthetic chemistry of polymers is the development of methods for controlled radical polymerization (Reversible Deactivation Radical Polymerization.). The advantages include the ability to control the molecular weight value of the polymers obtained by varying the ratio between the initiator and the monomer, as well as simultaneous fragment-by-fragment chain growth, which results in a narrow molecular weight distribution.
According to Ivan Grishin, head of the research laboratory for organic synthesis and radical processes at Lobachevsky University, UNN researchers work was aimed to develop a new method for producing acrylonitrile copolymer, which makes it possible to obtain a precursor for high-quality carbon fibers that feature high strength and elastic modulus. To obtain these acrylonitrile copolymers, the method of controlled Atom Transfer Radical Polymerization (ATRP) was used for the first time, with copper bromide as a catalyst. Due to the high initiation efficiency and the fragment-by-fragment chain growth, this method allows obtaining narrowly dispersed copolymers with specified molecular weights.
«As a result of our experiments, we obtained samples with molecular weights of more than 70 kDa and a narrow molecular weight distribution, which meets the requirements for copolymers to be processed into high-strength carbon fibers. The important advantages of the proposed method are the use of very low concentrations of the catalyst (at the level of hundredths of a percent), as well as the high rate of the process, which is due to the use of glucose as an activator,» said Ivan Grishin.
In the course of the research, copolymers were obtained that feature a high degree of compositional homogeneity, as well as a predetermined molecular weight value and composition. The effect of comonomers on the behavior of samples in the process of their oxidative stabilization was investigated. It is shown that by using the proposed composition based on three monomers (acrylonitrile, methyl acrylate and dimethyl itaconate) it is possible to achieve a significant reduction of the exothermic effect in the process of precursor oxidative stabilization, which has a favourable effect the mechanical properties of the resulting carbon fiber.
The composition and copolymerization method proposed by UNN scientists can be successfully used to produce acrylonitrile copolymers that can serve as precursors for high-strength carbon fibers.